Preparation and electrochemical performance of nitrogen-doped coal tar pitch-basedporous carbon by chemical foaming coupled with KOH activation

2023 No. 08
366
141
OnlineView
Download
Authors:
JIN Zhanzhan
HE He
SHI Feng
XING Baolin
HUANG Guangxu
ZHANG Chuanxiang
LIU Quanrun
Unit:
College of Chemistry and Chemical Engineering, Henan Polytechnic University
State Collaborative Innovation Center of Coal Work Safety and Clean-efficiency Utilization
Abstract:

Using the coal tar pitch as the carbon precursor, ammonium sulfate as the foaming agent and nitrogen source, and KOH as theactivator.Nitrogen-doped three-dimensional structured porous carbon was prepared by chemical foaming coupled with KOH activation.The microstructure and heteroatom content of coal tar pitch based porous carbon were controlled by adjusting the alkali carbon ratio and theeffects of alkali carbon ratio and heteroatom content on the performance of porous carbon were investigated. The structure and compositionof the materials were characterized by SEM, XPS, and N2 adsorption and desorption, and the electrochemical properties of the materialswere evaluated with Galvanostatic Charge-Discharge, Cyclic Voltammetry, and Electrochemical Impedance Spectroscopy. The results showthat chemical foaming coupled with KOH activation not only optimizes the internal pores to form a hierarchical pore structure and dopesthe carbon skeleton with an appropriate amount of heteroatoms, but also effectively improves the electrochemical performance of the por⁃ous carbon under the dual effect. The optimized NPC-2 shows a high specific surface area (1 636 m2 / g), abundant nitrogen (5.27%),and mutually cross-linked nitrogen - doped carbon skeleton. In the three - electrode system, the NPC - 2 electrode material obtains ahigh mass specific capacitance with a mass specific capacitance of 374.2 F/ g at a current density of 0.5 A/ g; when the current density isas high as 100 A/ g, its mass specific capacitance can still reach 249.5 F/ g and the capacitance retention rate can reach 66.7%, showingexcellent electrochemical performance. This excellent performance is derived from the well-developed graded pore structure and excel⁃lent carbon conductive network.

Keywords:
coal tar pitch
porous carbon
supercapacitor
chemical blowing
Citation format:
晋展展(1997—),男,河南焦作人,硕士研究生。E-mail:jinchuyan97@163.com
Chart:
Articles:
--
Citation format:
JIN Zhanzhan,HE He,SHI Feng,et al.Preparation and electrochemical performance of nitrogen-doped coal tar pitch-basedporous carbon by chemical foaming coupled with KOH activation[J].Clean Coal Technology,2023,29(8):65-72.

About Journal

  • Executive director

    China Coal Science and Industry Group Co., Ltd

  • Sponsored by

    Coal Science Research Institute Co., Ltd
    Coal Industry Clean Coal Engineering
    Technology Research Center

  • Editor in Chief

    XIE Qiang

  • Vice Editor-in-Chief

    YU Chang
    SHI Yixiang
    ZHAO Yongchun
    DUAN Linbo
    CAO Jingpei
    ZENG Jie

  • Publication Frequencies

    Monthly

  • ISSN

    1006-6772

  • CN

    11-3676/TD

Covered by

  • CSTPCD
  • RCCSE(A+)
  • AJ
  • EBSCO host
  • Ulrichsweb
  • JST
  • Scopus

Contact us

New Media

  • Meichuanmei
    Meichuanmei
  • Clean Coal Technology
    Clean Coal Technology
  • Online Journals
    Online Journals
Website Copyright © {year} Clean Coal Technology
京ICP备05086979号-19
地址:Coal Tower, Hepingli, Chaoyang District, Beijing, China.
邮编:100013
Tel:86-10-87986452 / 010-87986451
E-mail:jjmjs@263.net